air pressure thermal shock resistant Si3N4 bar stick
La reputazione dipende dalla qualità, la qualità proviene da dura!
Silicon Nitride Ceramic:
Liquid phase sintering is to add A1203 and Y 203 to the silicon carbide powder. After molding, it is sintered at 1800 °C to 2000 y. In the sintering process, A1z team and Y203 form eutectic compound YAG (aluminum garnet Y3Ali [ )) melting point 1760 ° C), the appearance of liquid phase promotes the sintering of Sic and Boron Nitride Ceramic reduces the sintering temperature. Abrasive water jet drilling ceramic technology research compared with cutting processing, drilling processing does not need to consider the influence of nozzle feed rate, processing There are two main problems in the process of relatively simple drilling processing: one is the control of the roughness of the hole wall and the size of the hole; the other is that due to the Zirconia Ceramic Rings divergence of the abrasive water jet, the hole formed by the machining will have a certain degree of inclination. Wan Qingfeng Through experiments, it can be concluded that the larger jet pressure, smaller nozzle traverse speed and proper abrasive flow can effectively increase the drilling depth and improve the quality of the hole wall. However, due to the jet divergence, the hole wall presents a certain taper and points. For the smooth drilling area and the deformation wear area, when the hole being machined is a blind hole, the bottom Machinable Ceramic part will be blocked by the [water pad", and the bag-like structure will be formed. The mathematical method is used to establish the prediction model of drilling depth and surface roughness of the hole wall. The research status and progress of the abrasive water jet processing ceramics respectively. The abrasive holes can be used to ream the existing holes. However, there is no relevant research literature in China. Subsequent research can be applied to the research of reaming processing technology to further broaden the application of abrasive water jet drilling.
Proprietà :
High hardness, high strength, wear resistance, corrosion resistance, high temperature(1200 ° ), good thermal diffusivity, good thermal shock resistance(avoid the temperature changing rapidly), good insulativity, low density. The comprehensive properties are best in most of structure ceramic.
Data Sheet↓
Color: Black Grey
Density: >3.2g/cm3
Hardness: HRA90
Vickers Hardness (Hv50): >1550 HV0.5
Modulus of Elasticity: 290Gpa
Flexural Strength: >600Mpa
Compressive Strength: 2500Mpa
Modulus of Elasticity(25°C): 65Gpa
Fracture toughness:>6.0 Mpam1/2
Maximum Use Temperature: 1200°C
Thermal Conductivity:15-20 W(mK)
Thermal Expansion Coefficient: >3.1 10-6/°C
Thermal Shock Resistance: 500 △T°C
Special Heat Capacity: 700 KJ/kg.K
Dielectric Strength: 1 KV/mm
Dielectric Constant: er
Volume Resistivity(20°C): 1.0*10(12)Ω.cm
Application industry :
Machinery, electronic, semiconductor, chemical, petroleum, smelt.
Specific application:
Welding shaft, electronic substrate, plunger, nozzle, slide guide, diesel parts, metal molding, shaft wheels etc.
Perché scegliere noi? 1,12 anni di fabbrica di ceramica industriale di produzione professionale 2. Prodotti di alta qualità a basso prezzo 3. Parti di precisione alta con la più bassa tolleranza 4. Tempo di scrupoli per la produzione 5. Ha un gruppo di team di ricerca e sviluppo esperto, professionale ed efficiente 6. È una buona reputazione in Cina e all'estero. 7.MOQ non è limitato, la piccola quantità è benvenuta.
8. Team vigous e buon servizio post-vendita
Show Products
FAQ
D: Sei la società o il produttore di trading?
A: Siamo fabbrica.
D: Quanto dura il tuo tempo di consegna?
A: Generalmente sono 5-10 giorni se la merce è disponibile. O sono 15-30 giorni se la merce non è in magazzino, è in base alla quantità.
D: Fornite campioni? È gratuito o extra?
A: Sì, potremmo offrire il campione gratuitamente ma non pagare il costo del trasporto merci.
D: Quali sono i tuoi termini di pagamento?
A: Pagamento <= 1000USD, in anticipo al 100%. Pagamento> = 1000USD, 50% T/T in anticipo, saldo prima dello shippment.